A Detailed Guide to Passivation For Stainless Steel
                            A Detailed Guide to Passivation For Stainless Steel 
What exactly do you mean by Passivation For Stainless Steel?
Passivation is a metal finishing technique used on stainless steel and other metal workpieces. It is a non-electrolytic chemical procedure that 
uses nitric or citric acid to form an outer layer of shield material and remove free iron from the surface. As a result, stainless steel parts are less 
likely to react with air and thus exhibit better corrosion resistance. Our Passivation For Stainless Steel process achieves a thicker chromium 
oxide layer as a result of removing free iron and increasing the chromium content in the metal, resulting in significantly improved corrosion 
resistance of steel and other metals.
Why should stainless steel grades get passivated?
Stainless steel naturally shows excellent corrosion resistance. 
However, it is not entirely immune to corrosion, especially rust. 
Stainless steel owes excellent corrosion resistance to the high 
chromium content in the alloy. Due to the chemical reaction of 
chromium & oxygen, stainless steel forms a thin protective layer of 
chromium oxide on the surface. However, small spots on the surface 
may rust despite the oxide layer, which happens because water 
molecules can oxidize some iron in the areas due to grain 
boundaries or foreign matter. This process is called rouging. The 
removal of the contaminants & the oxide growth process is known 
as passivation.
How does passivation work?
 
There are several other specifications for the passivation process of steel and other metals, depending on the different standards. 
Mostly, different passivation standards have a few steps in common, which are:
 The steel gets cleaned from foreign materials & particles of iron.
 The workpiece gets chemical treatment via immersion. This step takes place in the acid bath, usually nitric or citric acid.
 The stainless steel surface gets examined whether the chemical treatment was successful or not.
The passivation procedure accelerates the natural method, which occurs when the material gets exposed to oxygen in the atmosphere. Thus, 
passivation helps to build the inert oxide layer more quickly. Further, the build-up protective layer becomes significantly thicker than found in 
nature.
As already mentioned, all the different passivation specifications have the following steps every day. 
The first step in the passivation method is the cleaning of the workpiece. The steel must be immaculate of any contaminants. A validating test 
proves this circumstance. 
After the cleaning, all the parts are placed in an acidic passivating bath. Depending upon the stainless steel grade, one of these approaches can 
be used: nitric acid passivation, nitric acid with sodium dichromate passivation, & citric acid passivation. The time duration, which usually has a 
minimum of 20 to 30 minutes, & the temperature, which ranges from ambient to 60° C, are predetermined.
 Next, the parts are neutralized through a bath of aqueous sodium hydroxide. Finally, the stainless steel workpiece gets rinsed with clean water 
& then dried. The surface undergoes a testing task with humidity, elevated temperature, or salt spray to validate the passivation results. 
Martensitic stainless steel, however, must receive special treatment due to it being challenging to passivate.
Thus, choose Reba Safer Chemical for Passivation for Stainless Steel and keep your equipment safe from corrosion. If you want any information 
about Clean Rust From Stainless Steel, you are in the right place. Our team will guide you on this & explain the whole process.
Contact Us:- 
Website:- https://www.rebaaus.com/
Phone No:- +61 3 8526 8252
Address:- 1 Redwood Drive, Notting 
Hill, Victoria 3168, Australia